Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73GM40 NC010 DUPONT USA
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.50 kJ/m² |
| 23°C | ISO 179/1eA | 7 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.50 kJ/m² |
| Tensile modulus | ASTM D638/ISO 527 | 8300 kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO 527-2 | 8300 Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
| elongation at break | 23°C | ISO 527-2 | 3 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.00 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 140 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 500 V |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| Dissipation Factor | 23°C | IEC 60250 | 3.8E-03 1MHz |
| 23°C | IEC 60250 | 0.013 100HZ | |
| Volume resistivity | IEC 60093 | >1.0E+15 Ω.cm |
| other | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| characteristic | 低翘曲性 热稳定性良好 |
| Physical properties | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.46 |
| processability | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| Temperature | 70-120 °C |
| physical property | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| Water absorption rate | (23°C,50RH,2.00mm) | ISO 62 | 1.60 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.50 % |
| Water absorption rate | (23°C,24hr,2.00mm) | ISO 62 | 5.60 % |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 0.70 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73GM40 NC010 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 195 °C |
| vicat | ISO 306/B50 | 210 °C | |
| 熔融温度 | ISO 11357-3 | 221 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 215 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 70 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.7E-05 cm/cm/°C |