Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM KFL-4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Casters、household electrical appl
High temperature resistan、UV resistance、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4034 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4034 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 6500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 67.0 Mpa |
| bending strength | ISO 178 | 92.0 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.50 |
| Flexural modulus | ISO 178 | 5500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Wear factor | Washer | ASTM D3702Modified | 198 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.46 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4034 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4034 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 3.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 149 °C |