Certificates
ABS A3000 GY SABIC INNOVATIVE US
LNP™ STAT-KON™
electrical equipment
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 26.9 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 16 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 32.8 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2010 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.1 % |
| bending strength | ASTM D790 | 65.7 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.0 % |
| tensile strength | 断裂 | ASTM D638 | 36.7 Mpa |
| 断裂 | ISO 527-2 | 31.0 Mpa | |
| Flexural modulus | ASTM D790 | 2100 Mpa | |
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| bending strength | ISO 178 | 59.1 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 24 % |
| Flexural modulus | ISO 178 | 1980 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 39.1 Mpa |
| 屈服 | ISO 527-2 | 38.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+9to1.0E+11 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.41 % |
| MD：24小时 | ASTM D955 | 0.40 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 1.1 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.50 % |
| TD:24小时 | ISO 294-4 | 0.49 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/A3000 GY |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 91.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 88.9 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9.3E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 9.3E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 76.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 76.7 °C |