Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS SER22 DAICEL JAPAN
CEVIAN®
Home appliance components
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DAICEL JAPAN/SER22 |
|---|---|---|---|
| melt mass-flow rate | 220℃,10kg | ISO 1133 | 55 g/10min |
| Water absorption rate | ISO 62 | 0.3 % | |
| density | ISO 1183 | 1.20 |
| Electrical performance | Test Condition | Test Method | DAICEL JAPAN/SER22 |
|---|---|---|---|
| dielectric strength | 1.5mm | ASTM D-149 | 22 MV/m |
| arc resistance | 3.0mm | ASTM D-495 | PLC_6 |
| 3.0mm | ASTM D-495 | 66 sec |
| Mechanical properties | Test Condition | Test Method | DAICEL JAPAN/SER22 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30℃,6.4mm | ASTM D-256 | 80 J/m |
| tensile strength | ISO 527 | 44 Mpa | |
| Rockwell hardness | ISO 2039 | R114 | |
| bending strength | ISO 178 | 65 Mpa | |
| Flexural modulus | ISO 178 | 2100 Mpa | |
| Impact strength of cantilever beam gap | 23℃,6.4mm | ASTM D-256 | 140 J/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 14 KJ/m |
| -30℃ | ISO 179/1eA | 8 KJ/m |
| physical property | Test Condition | Test Method | DAICEL JAPAN/SER22 |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4-0.6 % |
| Thermal performance | Test Condition | Test Method | DAICEL JAPAN/SER22 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359 | 8 ×10 |
| Heat distortion temperature | 1.80MPa,12.7mm，HDT | ISO 75/A | 72 °C |
| vicat | 9.8N,50℃/h | ASTM D-1525 | 92 °C |
| combustibility | UL 94 | V-0 | |
| vicat | 50N,50℃/h | ISO 306/B50 | 82 °C |
| Heat distortion temperature | 1.82MPa,12.7mm，HDT | ASTM D-648 | 84 °C |
| Ball indentation temperature | 80 °C |