PA66 A175G15 UNITIKA JAPAN
UNITIKA
Vehicle electronics、Electrical components、Electronic field、Electrical field
Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/A175G15 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5700 Mpa | |
| Tensile stress | 断裂 | ISO 527-2 | 120 Mpa |
| Charpy Notched Impact Strength | ISO 179 | 30 kJ/m² | |
| bending strength | ISO 178 | 188 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 5000 Mpa |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/A175G15 |
|---|---|---|---|
| dielectric constant | 1MHZ | IEC 60250 | 3.4 |
| Volume resistivity | IEC 60093 | 1E+14 | |
| dielectric strength | 1.0mm | IEC 60243-1 | 33 |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/A175G15 |
|---|---|---|---|
| Shrinkage rate | MD，3.2mm | ISO 294-4 | 0.60 % |
| 横向，3.2mm | ISO 294-4 | 1.5 % | |
| Water absorption rate | 23℃，50%RH | ISO 62 | 1.9 % |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/A175G15 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 175-2/A | 229 °C |
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000042 cm/cm/℃ | |
| UL flame retardant rating | 0.840mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 175-2/B | 252 °C |