Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AES WH50 UMG JAPAN
DIALAC®
--
High hardness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/WH50 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 112 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/WH50 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 75.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2500 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2350 Mpa |
| tensile strength | 23°C | ISO 527-2 | 48.0 Mpa |
| physical property | Test Condition | Test Method | UMG JAPAN/WH50 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.70-0.80 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 5.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/WH50 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 78.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |