POM F20-02 KEP KOREA
KEPITAL®
Electrical field、Electronic field、Automotive sector、Electrical components、Application in the automo、Electronic data processin
wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 64 J/m |
| hardness | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 80 |
| Electrical performance | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 7E-03 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| Mechanical properties | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 90.0 Mpa |
| shear strength | 2.00mm | ASTM D732 | 55.0 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 61.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2600 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 60 % |
| flammability | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | HB |
| physical property | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 2.0 % |
| Water absorption rate | 平衡,23°C,60%RH | ASTM D570 | 0.22 % |
| density | ASTM D792 | 1.41 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | KEP KOREA/F20-02 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| 熔融温度，HDT | ASTM D648 | 165 °C | |
| Linear coefficient of thermal expansion | MD：20到80°C | ASTM D696 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 158 °C |