Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XANTAR® 19 UR Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 70 M（Scale） |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2400 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 2305 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 69.3 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 60 MPa |
| elongation at break | 23°C | ISO 527-2 | >50 % |
| bending strength | 23°C | ISO 178 | 90 MPa |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 9.2E-03 | |
| dielectric constant | IEC 60250 | 3.00 100Hz | |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 225 V |
| dielectric strength | IEC 60243-1 | 740 KV/mm | |
| dielectric constant | IEC 60250 | 2.90 1MHz | |
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| Dissipation Factor | IEC 60250 | 6.6E-04 100Hz | |
| Volume resistivity | IEC 60093 | >1.0E+15 Ω.cm |
| optical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| transmittance | μm | ISO 13468-2 | 89.0 ％ |
| Flame retardant performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| UL flame retardant rating | UL -94 | V-2 1.50mm | |
| UL -94 | V-2 3.00mm | ||
| UL -94 | V-2 0.75mm |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 0.976 in³/10min |
| Water absorption rate | (饱和,24hr) | ISO 62 | 0.35 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| Shrinkage rate | MD3.2mm | ISO 294-4 | 0.60 % |
| melt mass-flow rate | 特性粘数 | ISO 1628-4 | 1270 in³/lb |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 19 UR |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 130 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.6E-05 cm/cm／°C |
| 球压测试 | IEC 60695-10-2 | Pass | |
| 熔体导热系数 | 1.7 Btu·in/hr/ft²/°F | ||
| vicat | ISO 306/B50 | 145 °C |