Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HIPS PH-888H ZHENJIANG CHIMEI
POLYREX®
TV、Refrigerator、Video tape、Computer accessories、Electrical field、Electronic field、Electrical appliances
heat-resisting、High rigidity、High temperature resistan
SGS
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 97 J/m |
| 23°C,6.40mm | ASTM D256 | 83 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 5.2 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.5 kJ/m² |
| 23°C | ISO 180/1A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 63 |
| Mechanical properties | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 30.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 45 % |
| bending strength | --5 | ASTM D790 | 44.1 Mpa |
| --6 | ISO 178 | 39.0 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 50 % |
| tensile strength | 断裂4 | ASTM D638 | 29.4 Mpa |
| Flexural modulus | --6 | ISO 178 | 1500 Mpa |
| --5 | ASTM D790 | 1930 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 30.0 Mpa |
| flammability | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.8 g/10min |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| density | --3 | ASTM D792 | 1.05 g/cm³ |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 3.80 cm3/10min |
| Thermal performance | Test Condition | Test Method | ZHENJIANG CHIMEI/PH-888H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 82.0 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 97.0 °C | |
| 1.8MPa,退火，HDT | ISO 75-2/A | 96.0 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 79.0 °C | |
| vicat | -- | ASTMD15257 | 102 °C |
| -- | ISO 306/B50 | 92.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.0E-5到6.0E-5 cm/cm/°C |