ABS EX58F-NA1000 SABIC INNOVATIVE MEXICO
CYCOLAC™ 
Electrical appliances、Architectural application、Automotive interior parts
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
Dart impact23°C, Total EnergyASTM D376337.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
Rockwell hardnessR 级ASTM D785102
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
Tensile modulus--2ASTM D6382080 Mpa
tensile strength 屈服3ASTM D63839.0 Mpa
elongation断裂3ASTM D63832 %
断裂ISO 527-2/5021 %
Flexural modulus--5ISO 1782000 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79066.0 Mpa
--5,6ISO 17860.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902160 Mpa
tensile strength 断裂ISO 527-2/5030.0 Mpa
屈服ISO 527-2/5041.0 Mpa
elongation屈服ISO 527-2/502.6 %
屈服3ASTM D6383.1 %
tensile strength 断裂3ASTM D63830.0 Mpa
Tensile modulus--ISO 527-2/11970 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
Hot wire ignition (HWI)UL 746PLC 4
arc resistanceASTM D495PLC 5
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 1
Compared to the Leakage Tracking Index (CTI)UL 746PLC 0
High arc combustion index (HAI)UL 746PLC 4
flammabilityTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
UL flame retardant rating1.5 mmUL 94HB
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
melt viscosity240°C, 100 sec^-1ASTM D38351550 Pa·s
physical property Test ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
melt mass-flow rate220°C/10.0 kgISO 11334.0 g/10 min
Shrinkage rate3.20 mm，Flow内部方法0.60 - 0.80 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE MEXICO/EX58F-NA1000
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8311.0E-4 cm/cm/°C
vicat--ISO 306/B12097.0 °C
--ASTM D15259106 °C
--ISO 306/B5095.0 °C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D64891.0 °C
RTI ImpUL 74660.0 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDTISO 75-2/Af78.0 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8311.0E-4 cm/cm/°C
RTIUL 74660.0 °C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D64876.0 °C
RTI ElecUL 74660.0 °C