PC/PBT 5220U-7A1D007 SABIC INNOVATIVE SHANGHAI

XENOY™

Electronic accessories

UV resistance,Antichemical

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	75.0 °C
		0.45 MPa, Unannealed, 6.40 mm	ASTM D648	107 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	9.0E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	9.5E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
RTI		UL 746	75.0 °C
RTI Elec		UL 746	75.0 °C
RTI Imp		UL 746	75.0 °C
Vicat softening temperature	--	ISO 306/B120	125 °C
		--	ISO 306/B50	120 °C
		--	ASTM D152511	122 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
Bending modulus	--7	ISO 178	2000 Mpa
Bending modulus		50.0 mm Span6	ASTM D790	2030 Mpa
bending strength	--7,8	ISO 178	80.0 Mpa
bending strength		Yield, 50.0 mm Span6	ASTM D790	84.0 Mpa
elongation	Yield	ISO 527-2/50	4.0 %
		Yield5	ASTM D638	4.0 %
		Break5	ASTM D638	120 %
		Break	ISO 527-2/50	120 %
Tensile modulus	--4	ASTM D638	2250 Mpa
		--3	ASTM D638	2250 Mpa
		--	ISO 527-2/1	2050 Mpa
tensile strength	Yield	ISO 527-2/50	50.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Break5	ASTM D638	51.0 Mpa
		Yield5	ASTM D638	53.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		UL 746	PLC 1
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
melt mass-flow rate	250°C/5.0 kg	ISO 1133	16 g/10 min
Melt Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	15.0 cm3/10min
Outdoor applicability		UL 746C	f2
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.80 - 1.0 %
Shrinkage rate		Across FlowFlow 2	Internal Method	0.80 - 1.0 %
Specific volume		ASTM D792	0.830 cm³/g
Water absorption rate	Saturation, 23°C	ISO 62	0.50 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.15 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
Dart impact	23°C, Total Energy	ASTM D3763	60.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
UL flame retardant rating	1.5 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-7A1D007
Back pressure			0.300 to 0.700 Mpa
drying temperature			110 °C
drying time			4.0 to 6.0 hr
Exhaust hole depth			0.013 to 0.020 mm
Mold temperature			65 to 90 °C
Processing (melt) temperature			260 to 275 °C
Screw speed			50 to 80 rpm
Spray nozzle temperature			255 to 270 °C
Suggested injection volume			50 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			255 to 275 °C
Temperature at the rear of the barrel			245 to 265 °C
Temperature in the middle of the barrel			250 to 270 °C