Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC OQ1020C-112 SABIC INNOVATIVE JAPAN
LEXAN™
--
Optical applications、optics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/OQ1020C-112 |
|---|---|---|---|
| transparency | ASTM D-1003 | 90 |
| Basic performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/OQ1020C-112 |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 70 g/10min |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/OQ1020C-112 |
|---|---|---|---|
| Flexural modulus | ASTM D-790 | 2067 Mpa | |
| elongation at break | 断裂点 | ASTM D-638 | 40 % |
| Impact strength of cantilever beam gap | 缺口23°C | ASTM D-256 | 267 J/m |
| tensile strength | 屈伏点 | ASTM D-638 | 63 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/OQ1020C-112 |
|---|---|---|---|
| Shrinkage rate | 3.2mm | ASTM D-955 | 5-7 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/OQ1020C-112 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa，HDT | ASTM D-648 | 121 °C |