PC S-2000VR BK MITSUBISHI THAILAND
IUPILON™
Automotive sector、Casters、Electrical appliances
UV resistance、transparent、enhance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/S-2000VR BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 76 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/S-2000VR BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 110 % | |
| bending strength | ISO 178 | 93.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.6 % |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/S-2000VR BK |
|---|---|---|---|
| dielectric strength | 1.00mm | IEC 60243-1 | 31 KV/mm |
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-04 |
| dielectric strength | 3.00mm | IEC 60243-1 | 18 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | 6E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/S-2000VR BK |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.50-0.70 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.24 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/S-2000VR BK |
|---|---|---|---|
| 1.8MPa, Not annealed | ISO 75-2/A | 129 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| 0.45MPa, Not annealed | ISO 75-2/B | 143 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6.6E-05 cm/cm/°C |