Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G3000HR BK34 INVISTA SHANGHAI
INVISTA™
--
Filler: Glass fiber reinf、Good dimensional stabilit、High tensile strength、Hydrolysis resistance、thermal stability、Good demolding performanc、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | INVISTA SHANGHAI/G3000HR BK34 |
|---|---|---|---|
| tensile breaking strength | ISO 527 | 195 Mpa | |
| Bending stress | ISO178 | 270 Mpa | |
| Tensile modulus | ISO527-2 | 9800 Mpa | |
| ISO 527 | 9800 Mpa | ||
| Tensile strain | 断裂 | ISO527-2 | 3.1 % |
| Charpy Notched Impact Strength | -40℃ | ISO 179 | 9.0 kJ/m² |
| Tensile stress | 断裂 | ISO527-2 | 195 Mpa |
| bending strength | ISO 178 | 270 Mpa | |
| Flexural modulus | ISO 178 | 9100 Mpa | |
| ISO178 | 9100 Mpa | ||
| Elongation | ISO 527 | 3.1 % | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 10 kJ/m² |
| physical property | Test Condition | Test Method | INVISTA SHANGHAI/G3000HR BK34 |
|---|---|---|---|
| Shrinkage rate | MD: 2.00 mm | ISO 294-4 | 0.30-0.40 % |
| MD:2.00mm | ISO294-4 | 0.30to0.40 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 1.8 % |
| Shrinkage rate | TD: 2.00 mm | ISO 294-4 | 0.95-1.05 % |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 1.2 % |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 0.95to1.1 % |
| Water absorption rate | 23°C,24hr | ISO62 | 1.2 % |
| 平衡, 23℃, 50% RH | ISO 62 | 1.8 % |
| Thermal performance | Test Condition | Test Method | INVISTA SHANGHAI/G3000HR BK34 |
|---|---|---|---|
| Melting temperature | 10 ℃/min | ISO 11357 | 262 °C |
| 0.45 MPa, 未退火 | ISO 75 | 255 °C | |
| 0.45MPa,未退火 | ISO75-2/B | 255 °C | |
| 1.82 MPa, 未退火 | ISO 75 | 248 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 248 °C | |
| melting temperature | ISO11357-3 | 262 °C |