Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS G-10 BK TOSOH JAPAN
SUSTEEL®
Automotive sector、Casters、Electronic field、Electrical field
Glass fiber reinforced、enhance、Filler: Glass mineral
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 210 J/m |
| Supplementary Information | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| BarFlowLength | 1.00mm | 内部方法 | 125 mm |
| hardness | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Basic performance | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| density | ASTM D-792 | 1.94 |
| Mechanical properties | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 0.60 % |
| Charpy Notched Impact Strength | 有缺口 | ASTM D-256 | 64 J/m |
| bending strength | ASTM D790 | 221 Mpa | |
| ASTM D-790 | 225 Mpa | ||
| Charpy Notched Impact Strength | 无缺口 | ASTM D-256 | 206 J/m |
| Tensile Weld Strength | ASTM D638 | 39.0 Mpa | |
| tensile strength | ASTM D-638 | 123 Mpa | |
| Rockwell hardness | ASTM D-785 | 121 | |
| Flexural modulus | ASTM D-790 | 20 GPa | |
| elongation at break | ASTM D-638 | 0.8 % | |
| Flexural modulus | ASTM D790 | 20000 Mpa | |
| tensile strength | ASTM D638 | 116 Mpa |
| Electrical performance | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| Dissipation Factor | 1MHz | ASTM D-150 | 0.0015 |
| thermal conductivity | 自定标准 | 0.48 W/m.K | |
| Volume resistivity | ASTM D257 | 1E+18 ohms·cm | |
| ASTM D-257 | 4×1016 Ω.cm | ||
| dielectric constant | 1MHz | ASTM D-150 | 4.9 |
| Dissipation Factor | 1MHz | ASTM D150 | 1.5E-03 |
| dielectric strength | ASTM D-149 | 14 KV/mm | |
| ASTM D149 | 15 KV/mm | ||
| dielectric constant | 1MHz | ASTM D150 | 4.90 |
| arc resistance | ASTM D495 | 150 sec |
| processability | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| Shrinkage rate | 垂直方向 | ASTM D-955 | 0.6 % |
| 流动方向 | ASTM D-955 | 0.3 % |
| flammability | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| melt mass-flow rate | 315°C/5.0kg | ASTM D1238 | 90 g/10min |
| Shrinkage rate | MD | 内部方法 | 0.30 % |
| Water absorption rate | 平衡 | ASTM D570 | >0.020 % |
| Shrinkage rate | TD | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | TOSOH JAPAN/G-10 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | >260 °C |
| melting temperature | 内部方法 | 285 °C | |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | ＞260 °C |
| Linear coefficient of thermal expansion | 自定标准 | 2 | |
| UL flame retardant rating | UL 94 | V-0 |