Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP EE137AI BOREALIS EUROPE
Daplen™
Automotive sector
filling
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | BOREALIS EUROPE/EE137AI |
|---|---|---|---|
| melt mass-flow rate | 230℃,2.16kg | ISO 1133 | 12 g/10min |
| 230℃,5kg | ISO 1133 | 45 g/10min | |
| density | ISO 1183 | 0.96 g/cm |
| Mechanical properties | Test Condition | Test Method | BOREALIS EUROPE/EE137AI |
|---|---|---|---|
| tensile strength | 50mm/min | ISO 527-2 | 21 Mpa |
| elongation | 50mm/min | ISO 527-2 | 6 % |
| Impact strength of cantilever beam gap | ISO 180/1A | 25 KJ/m | |
| Tensile modulus | 1mm/min | ISO 527-2 | 1850 Mpa |
| ball-indentation hardness | H385/30 | ISO 2039 | 42 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 1700 Mpa |
| physical property | Test Condition | Test Method | BOREALIS EUROPE/EE137AI |
|---|---|---|---|
| Shrinkage rate | Borealis Method | 0.0011 cm/cm |
| Thermal performance | Test Condition | Test Method | BOREALIS EUROPE/EE137AI |
|---|---|---|---|
| Temperature | 30-50 °C | ||
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-2 | 55 °C |
| vicat | B(10N) | ISO 306 | 54 °C |
| melting temperature | 220-260 °C | ||
| Heat distortion temperature | 0.46MPa，HDT | ISO 75-2 | 100 °C |
| vicat | A(10N) | ISO 306 | 136 °C |