PA6 1010GN2-30 MITSUBISHI ENGINEERING JAPAN
Novamid®
Electronic and Electrical
enhance、Glass fiber reinforced、Flame retardant、Glass reinforcement、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1010GN2-30 |
|---|---|---|---|
| bending strength | D790 | 1890(1000) Kgf/cm | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 54(160) J/m |
| Stretching length | D638 | 5(7) % | |
| bending strength | D790 | 185(98) Mpa | |
| tensile strength | D638 | 1400(900) Kgf/cm | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 5.5(16) Kgf.cm/cm |
| Flexural modulus | D790 | 9.16(5.10) GPa | |
| Impact strength of cantilever beam gap | 1/8寸 | D256 | 6.9(30) Kgf.cm/cm |
| 1/8寸 | D256 | 68(290) J/m | |
| tensile strength | D638 | 140(88) Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1010GN2-30 |
|---|---|---|---|
| Dielectric loss | 正切 | D150 | 0.02(0.1) |
| arc resistance | ℃ | 120-130 S | |
| dielectric strength | D149 | 15(15) MV/m | |
| dielectric constant | D150 | 35-53(88) Pf/m |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1010GN2-30 |
|---|---|---|---|
| Rockwell hardness | D785 | 120(115) R | |
| Shrinkage rate | 0.2/0.4 MD% | ||
| coefficient of friction | D1894 | 0.35 | |
| Taber wear resistance | D1044 | 15 mg/1000cy | |
| Water absorption rate | D570 | 2.5 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1010GN2-30 |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 219 °C |
| Linear coefficient of thermal expansion | D696 | 4 | |
| UL flame retardant rating | UL 94 | V-0 |