PCTA MN611 EASTMAN USA
DuraStar™
food、chip
High mobility、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -40°C | ASTM D4812 | 无断裂 |
| -40°C | -40℃ | ASTM D256 | 40 J/m |
| 23°C | ASTM D256 | 80 J/m | |
| ISO 180 | 7.8 kJ/m² | ||
| -40°C | -40℃ | ISO 180 | 4.8 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 48.0 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 42.0 J |
| hardness | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 103 |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| Surrender, 23 ° C | ASTM D790 | 69.0 Mpa | |
| Fracture, 23 ° C | ASTM D638 | 51.0 Mpa | |
| ISO 527-2 | 46.0 Mpa | ||
| Surrender, 23 ° C | ASTM D638 | 5.0 % | |
| ISO 527-2 | 4.0 % | ||
| ASTMD638 | 47.0 Mpa | ||
| Tensile modulus | 23°C | ISO 527-2 | 1800 Mpa |
| 23°C | ISO 178 | 1850 Mpa | |
| Fracture, 23 ° C | ASTM D638 | 300 % | |
| ISO 527-2 | 200 % | ||
| 23°C | ASTM D790 | 2000 Mpa |
| optical performance | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| transmissivity | 总计 | ASTM D1003 | 91.0 % |
| Haze ratio | ASTM D1003 | 0.30 % | |
| transmissivity | 常规 | ASTM D1003 | 89.0 % |
| physical property | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20-0.60 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/MN611 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 74.0 °C |