LLDPE 2114 FPC TAIWAN
TAISOX®
film
high strength,High impact resistance,Heat sealing performance,Feature: Super C6,Good heat sealing perform,Ultra high impact strengt,Ultra high puncture stren,Speak well
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | FPC TAIWAN/2114 |
---|---|---|---|
lubrication prescription | 高 | ||
gloss | 45℃ | ASTM D-2457 | 51 % |
Haze ratio | ASTM D-1003 | 15 % | |
antiblocking agent | 高 | ||
transparency | 60 % |
Basic performance | Test Condition | Test Method | FPC TAIWAN/2114 |
---|---|---|---|
density | ASTM D-1505 | 0.918 g/cm | |
melt mass-flow rate | ASTM D-1238 | 1.0 g/10min |
Mechanical properties | Test Condition | Test Method | FPC TAIWAN/2114 |
---|---|---|---|
Dart impact | ASTM D-1709 | 610 g | |
tensile strength | TD,断裂 | ASTM D-882B | 450 kg/cm |
Tensile strength reduction | TD | ASTM D-882B | 110 kg/cm |
tear strength | TD | ASTM D-1922 | 500 g/25µm |
elongation at break | MD | ASTM D-882B | 620 % |
tensile strength | MD,断裂 | ASTM D-882B | 500 kg/cm |
Flexural modulus | TD,1%伸长率 | ASTM D-882B | 2000 kg/cm |
MD,1%伸长率 | ASTM D-882B | 1600 kg/cm | |
tear strength | MD | ASTM D-1922 | 305 g/25µm |
Tensile strength reduction | MD | ASTM D-882B | 100 kg/cm |
elongation at break | TD | ASTM D-882B | 810 % |
Thermal performance | Test Condition | Test Method | FPC TAIWAN/2114 |
---|---|---|---|
vicat | ASTM D-1525 | 93 °C | |
melting temperature | DSC | 121 °C |