Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF503R-701 SABIC INNOVATIVE SHANGHAI
LEXAN™
fibre
High impact resistance、High rigidity、Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/HF503R-701 |
|---|---|---|---|
| 23°C | ISO 180/1A | 10 kJ/m² | |
| ASTM D256 | 100 J/m | ||
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| -30°C | ISO 180/1A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/HF503R-701 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 15 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 100 Mpa |
| tensile strength | 断裂 | ASTM D638 | 53.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3440 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/HF503R-701 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 18 KV/mm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/HF503R-701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.31 % |
| Specific volume | ASTM D792 | 0.800 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/HF503R-701 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 142 °C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| vicat | ASTM D15257 | 154 °C |