PPO WCD835 BK1066 SABIC INNOVATIVE NANSHA
FLEX NORYL™
Electronic and Electrical、Automotive components
Non enhanced、Low odor
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| Shore hardness | 邵氏A,30秒 | ASTM D2240 | 83 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 9E+15 ohms·cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 40.0 Mpa |
| tensile strength | 断裂 | CCP METHOD | 17.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 250 % |
| Break,113°C3 | CCP METHOD | 250 % | |
| Flexural modulus | ISO 178 | 35.0 Mpa | |
| tensile strength | 断裂2 | ASTM D638 | 10.0 Mpa |
| elongation | 断裂 | CCP METHOD | 270 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 230 % |
| tensile strength | 断裂 | ISO 527-2/50 | 10.0 Mpa |
| Break,113°C3 | CCP METHOD | 18.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 850 °C |
| VW | CCP METHOD | Pass | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 750 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/WCD835 BK1066 |
|---|---|---|---|
| UL temperature rating | CCP METHOD | 80 °C | |
| brittle temperature | ASTM D746 | <-40.0 °C | |
| Heat distortion temperature | 100°C | CCP METHOD | 20 % |