PBT B 4406 G2 BASF GERMANY
Ultradur®
Lighting applications、switch、Laptop case、Shell
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| ISOType | ISO 7792 | PBT.MFGHLNR.11-060.GF10 |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | ASTM D257/IEC 60093 | 1E 14 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | - kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 5500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| tensile strength | 断裂 | ISO 527-2 | 95.0 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 5500 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| purpose | 高刚度和强度、尺寸稳定性、低吸水率和耐化学性.耐侯性和抗热老化性；应用于高性能领域.如不同工业部门中的承重部分 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1500 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.4 % |
| flammability | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| physical property | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| Apparent density | 0.70to0.80 g/cm³ | ||
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 15.0 cm3/10min |
| viscosity number | ISO 307 | 120 cm³/g | |
| Shrinkage rate | MD | 0.60 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | TD | 1.3 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4406 G2 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1600 mm/mm.℃ |