Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 330R ZEON JAPAN
ZEONEX®
pipeline、Automotive Applications
Ozone resistant、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2750 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 3100 Mpa | |
| elongation | ASTM D638/ISO 527 | 2 % | |
| Tensile modulus | ASTM D638/ISO 527 | 1770 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 32 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 45.0 Mpa |
| optical performance | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 92.0 % |
| Fuzzy coefficient (Haze) | ISO 14782 | - % | |
| refractive index | ASTM D542/ISO 489 | 1.509 | |
| ASTM D542 | 1.509 | ||
| gloss | - | ||
| transmittance | ASTM D1003/ISO 13468 | 92 % |
| other | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| characteristic | 耐化学系.防潮.抗紫外线良好.良好的成型性能。 | ||
| Color | 透明 | ||
| purpose | 光学应用、相机、印刷机。 |
| Physical properties | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | - % | |
| density | ASTM D792/ISO 1183 | 0.948 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | - g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| physical property | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | JISK6719 | 12 g/10min |
| Water absorption rate | 平衡 | ASTM D570 | <0.010 % |
| Thermal performance | Test Condition | Test Method | ZEON JAPAN/330R |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Glass Transition Temperature | JISK7121 | 123 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | - ℃（℉） |
| Glass Transition Temperature | ASTM D785 | 123 ℃（℉） | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 7E-05 cm/cm/°C |