HDPE SNOLEN® EM 3.3/58 JSC Gazprom neftekhim Salavat
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EM 3.3/58 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 23 kJ/m² |
| hardness | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EM 3.3/58 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 62 |
| Mechanical properties | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EM 3.3/58 |
|---|---|---|---|
| fracture | ISO 527-2/50 | >1000 % | |
| yield | ISO 527-2 | 10 % | |
| Tensile modulus | 23°C，正割 | ISO 527-2/1 | 1200 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 27.0 MPa |
| 断裂 | ISO 527-2/50 | 31.0 MPa |
| physical property | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EM 3.3/58 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.954to0.958 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 2.3to3.3 g/10min |
| Melt flow ratio | 8.00to12.0 | ||
| Environmental stress cracking resistance | 80°C,2%Arkopal | ISO 16770 | 2.00 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 23to33 g/10min |
| Thermal performance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EM 3.3/58 |
|---|---|---|---|
| vicat | ISO 306/B50 | 80.0 °C | |
| brittle temperature | ASTM D746 | <-80.0 °C |