Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BFL4000 WH3150 SABIC INNOVATIVE US
LEXAN™
Electrical applications、Lighting applications
Thermal stability、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 30 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 240 J/m |
| 23°C | ASTM D256 | 470 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 68.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 20 kJ/m² |
| 23°C | ISO 180/1A | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2040 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 44.0 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 47.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2050 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 50.0 Mpa |
| Tensile modulus | ASTM D638 | 2240 Mpa | |
| elongation | 断裂 | ASTM D638 | 56 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 90.0 Mpa |
| ISO 178 | 83.0 Mpa | ||
| Flexural modulus | ISO 178 | 2170 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 74 % |
| tensile strength | 屈服 | ASTM D638 | 54.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 22.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| density | ASTM D792 | 1.38 g/cm³ | |
| ISO 1183 | 1.38 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 24 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 124 °C |
| 1.8MPa,退火,3.20mm，HDT | ASTM D648 | 115 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 131 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| vicat | ASTM D152510 | 136 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 134 °C |
| 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 130 °C | |
| vicat | -- | ISO 306/B120 | 139 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 137 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 115 °C |