PC LDS 3730/13701 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Phone,Laser beacon
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
23°CISO 179/1eUNoBreak
Multi axis Instrumented Impact Energy-20°C2内部方法25.0 J
23°CISO 6603-235.0 J
23°C2内部方法25.0 J
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Tensile modulusISO 527-22200 Mpa
Nominal tensile fracture strainISO 527-2>50 %
bending strengthISO 17880.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-25.0 %
tensile strength 屈服ISO 527-252.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
dielectric constant1.00GHzIEC 602502.90
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dissipation Factor1.00GHzIEC 602505E-03
Surface ResistivityIEC 60093>1.0E+15 ohms
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
UL flame retardant rating3.0mmIEC 60695-11-10,-205VB
1.5mmIEC 60695-11-10,-20V-0
0.50mmIEC 60695-11-10,-20HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Shrinkage rateMDISO 294-40.60 %
Water absorption rate平衡,23°C,50%RHISO 620.35 %
Melt volume flow rate260°C/5.0kgISO 113310.0 cm3/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
vicatISO 306/B50145 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A122 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C