POM LU-02 CF2001 JAPAN POLYPLASTIC
DURACON®
Bottle cap、Electronic and electrical
UV resistance、Weather resistance、Low gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.8 kJ/m² |
Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
ColorNumber | CF2001 |
hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
Rockwell hardness | M计秤 | ISO 2039-2 | 80 |
Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
coefficient of friction | 与钢-动态4 | JISK7218 | 0.70 |
Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 1000 10^-8mm³/N·m |
Tensile modulus | ISO 527-2 | 2450 Mpa | |
Wear factor | 0.060MPa,0.15m/sec8 | JISK7218 | 7200 10^-8mm³/N·m |
Nominal tensile fracture strain | ISO 527-2 | 14 % | |
Wear factor | 0.49MPa,0.30m/sec5 | JISK7218 | <1.0 10^-8mm³/N·m |
bending strength | ISO 178 | 75.0 Mpa | |
Wear factor | 0.49MPa,0.30m/sec6 | JISK7218 | 200 10^-8mm³/N·m |
Flexural modulus | ISO 178 | 2250 Mpa | |
coefficient of friction | Dynamic3 | JISK7218 | 0.37 |
tensile strength | ISO 527-2 | 57.0 Mpa |
Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
Volume resistivity | IEC 60093 | 5E+13 ohms·cm | |
Surface Resistivity | IEC 60093 | 6E+15 ohms |
flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 19.0 cm3/10min |
Water absorption rate | 23°C,24hr | ISO 62 | 0.50 % |
density | ISO 1183 | 1.39 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 22 g/10min |
Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/LU-02 CF2001 |
---|---|---|---|
Linear coefficient of thermal expansion | TD:23到55°C | 内部方法 | 1.2E-04 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 82.0 °C |
Linear coefficient of thermal expansion | MD:23到55°C | 内部方法 | 1.2E-04 cm/cm/°C |