Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 7H2W-V0 LATI ITALY
LATENE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 25 kJ/m² |
| -20°C | ISO 179/1eU | 20 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| dimensional stability | 70.0 |
| Mechanical properties | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| Tensile modulus | 60°C | ISO 527-2/1 | 800 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 20 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 15.0 Mpa |
| Tensile strain | 屈服,60°C | ISO 527-2/5 | >10 % |
| Tensile modulus | 90°C | ISO 527-2/1 | 500 Mpa |
| 23°C | ISO 527-2/1 | 1800 Mpa | |
| tensile strength | 屈服,90°C | ISO 527-2/5 | 7.00 Mpa |
| Tensile strain | 屈服,90°C | ISO 527-2/5 | >10 % |
| 断裂,60°C | ISO 527-2/5 | >100 % | |
| tensile strength | 屈服,60°C | ISO 527-2/5 | 10.0 Mpa |
| Tensile strain | 断裂,90°C | ISO 527-2/5 | >100 % |
| 屈服,23°C | ISO 527-2/5 | 5.0 % | |
| tensile strength | 屈服,23°C | ISO 527-2/5 | 20.0 Mpa |
| Electrical performance | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| 2.0mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 33 % |
| physical property | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 1.2-1.5 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.2-1.5 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/7H2W-V0 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 110 °C |
| vicat | ISO 306/B50 | 100 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| Continuous use temperature | 100 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 8E-05 cm/cm/°C |