Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 5720U-YW5E108 SABIC INNOVATIVE US
XENOY™
Plastic bag、Lighting applications、Household daily necessiti
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/5720U-YW5E108
Melt Volume-Flow Rate (MVR)
250°C/2.16 kg
ISO 1133
cm3/10min
3
Melt Volume-Flow Rate (MVR)
250°C/5.0 kg
ISO 1133
cm3/10min
1
Melt Volume-Flow Rate (MVR)
265°C/2.16 kg
ISO 1133
cm3/10min
6
Melt Volume-Flow Rate (MVR)
265°C/5.0 kg
ISO 1133
cm3/10min
1
Melt mass flow rate
250°C/2.16 kg
ASTM D1238
g/10 min
3
Melt mass flow rate
250°C/5.0 kg
ASTM D1238, ISO 1133
g/10 min
1
Melt mass flow rate
265°C/2.16 kg
ASTM D1238
g/10 min
6
Melt mass flow rate
266°C/5.0 kg
ASTM D1238
g/10 min
2
Melt mass flow rate
250°C/2.16 kg
ISO 1133
g/10 min
3
Shrinkage rate - flow
3.20 mm
内部方法
%
1
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/5720U-YW5E108
Impact strength of simply supported beam gap
-30°C
ISO 179/1eA
kJ/m²
4
Impact strength of simply supported beam gap
23°C
ISO 179/1eA
kJ/m²
5
Tensile modulus
-- 2
ASTM D638
Mpa
1
Tensile modulus
-- 3
内部方法
Mpa
1
Tensile modulus
-- 4
ASTM D638
Mpa
1
Tensile modulus
--
ISO 527-2/1
Mpa
1
tensile strength
屈服 5
ASTM D638
Mpa
4
tensile strength
屈服 6
内部方法
Mpa
4
tensile strength
屈服 7
ASTM D638
Mpa
4
tensile strength
屈服
ISO 527-2/5
Mpa
4
tensile strength
屈服
ISO 527-2/50
Mpa
4
tensile strength
断裂 7
ASTM D638
Mpa
5
tensile strength
断裂 6
内部方法
Mpa
4
tensile strength
断裂 5
ASTM D638
Mpa
4
tensile strength
断裂
ISO 527-2/5, ISO 527-2/50
Mpa
4
elongation
屈服 7
ASTM D638
%
4
elongation
屈服 6
内部方法
%
4
elongation
屈服 5
ASTM D638
%
4
elongation
屈服
ISO 527-2/5
%
4
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 7
ASTM D638
%
1
elongation
断裂 6
内部方法
%
1
elongation
断裂 5
ASTM D638
%
1
elongation
断裂
ISO 527-2/5
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 8
ASTM D790
Mpa
1
Bending modulus
-- 9
ISO 178
Mpa
1
bending strength
-- 9, 10
ISO 178
Mpa
7
bending strength
屈服, 50.0 mm 跨距 8
ASTM D790
Mpa
7
bending strength
断裂, 50.0 mm 跨距 8
ASTM D790
Mpa
6
Dart impact equipped with measuring instruments
-40°C, Energy at Peak
ASTM D3763
J
4
Dart impact equipped with measuring instruments
-40°C, Total Energy
ASTM D3763
J
5
Dart impact equipped with measuring instruments
-30°C, Energy at Peak
ASTM D3763
J
4
Dart impact equipped with measuring instruments
-30°C, Total Energy
ASTM D3763
J
6
Dart impact equipped with measuring instruments
-20°C, Energy at Peak
ASTM D3763
J
4
Dart impact equipped with measuring instruments
-20°C, Total Energy
ASTM D3763
J
5
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
4
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/5720U-YW5E108
Hot deformation temperature
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Hot deformation temperature
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Hot deformation temperature
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12
ISO 75-2/Bf
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
8
Hot deformation temperature
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
9
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12
ISO 75-2/Af
°C
8
vicat softening point
--
ASTM D152513, ISO 306/B5013
°C
1
vicat softening point
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 95°C
ASTM E831
cm/cm/°C
9
Linear coefficient of thermal expansion
流动 : -30 到 80°C
ISO 11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
横向 : -40 到 95°C
ASTM E831
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : -30 到 80°C
ISO 11359-2
cm/cm/°C
1
Contact Us