PA66 Vydyne® 22HSP NT 美国奥升德（首诺）
--
衬套,轴承,外壳,凸轮,工业应用,连接器
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest Method美国奥升德（首诺）/Vydyne® 22HSP NT
Tensile modulus泊松比ISO 527-20.40
tensile strength 屈服,23°CISO 527-285 MPa
Tensile modulus23°CISO 527-23100 MPa
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A5.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNB kJ/m²
elongation at break屈服,23°CISO 527-25.0 %
Flexural modulus23°CISO 1782900 MPa
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A6.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNB kJ/m²
tensile strength 23°CISO 527-255 MPa
elongation at break23°CISO 527-225 %
bending strength23°CISO 17895 MPa
Electrical performanceTest ConditionTest Method美国奥升德（首诺）/Vydyne® 22HSP NT
Dissipation Factor相对漏电起痕指数IEC 60112400-599 V
耐电弧性IEC 6162160-119 s
Flame retardant performanceTest ConditionTest Method美国奥升德（首诺）/Vydyne® 22HSP NT
Limiting Oxygen IndexISO 4589-223 %
UL flame retardant ratingUL -94V-2 0.71mm
UL -94V-2 1.50mm
UL -94V-2 3.00mm
physical property Test ConditionTest Method美国奥升德（首诺）/Vydyne® 22HSP NT
Water absorption rate(23°C,24hr)ISO 621.2 %
Shrinkage rateMD2.0mmISO 294-42.0 %
densityISO 11831.14 g/cm³
Water absorption rate(23°C,50RH)ISO 622.4 %
Shrinkage rateTD2.0mmISO 294-42.2 %
Thermal performanceTest ConditionTest Method美国奥升德（首诺）/Vydyne® 22HSP NT
Hot deformation temperature (HDT)0.45MPa未退火，HDTISO 75-2/Bf200 °C
MDISO 11359-21E-05 cm/cm／°C
Hot deformation temperature (HDT)1.80MPa退火，HDTISO 75-2/Af70 °C
TDISO 11359-21E-05 cm/cm／°C
linear expansion coefficient熔点ISO 11359-2260 °C