PPS 6162A7 CELANESE USA
FORTRON®
Electrical applications,Automotive Applications
High mobility,Filler: Glass mineral
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 18 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 16 kJ/m² |
| -30°C | ISO 179/1eU | 28 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| relative permittivity | 1MHz | IEC 60250 | 5.68 |
| Dissipation Factor | 1MHz | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 15400 Mpa | |
| bending strength | 23°C | ISO 178 | 185 Mpa |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 115 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.3 % |
| Fracture bending strain | ISO 178 | 1.5 % |
| flammability | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.40-0.80 % |
| MD | ISO 294-4 | 0.10-0.30 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.017 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/6162A7 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 270 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 215 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3.4E-05 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 90.0 °C |