Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 6013M-07 TOPAS GERMANY
TOPAS®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TOPAS GERMANY/6013M-07 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 14 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TOPAS GERMANY/6013M-07 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 2.6 % |
| Tensile modulus | ISO 527-2/1A/1 | 2900 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 63.0 Mpa |
| optical performance | Test Condition | Test Method | TOPAS GERMANY/6013M-07 |
|---|---|---|---|
| transmissivity | ISO 13468-2 | 91.0 % | |
| refractive index | ISO 489 | 1.530 |
| physical property | Test Condition | Test Method | TOPAS GERMANY/6013M-07 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.010 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | TOPAS GERMANY/6013M-07 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 130 °C |
| Glass Transition Temperature | ISO 11357-2 | 142 °C |