PC/ABS LS-1150G Samsung Cheil South Korea
INFINO®
Electronic and Electrical、TV
enhance、Flame retardant、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.9 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.2 kJ/m² |
| 23°C,3.18mm | ASTM D256 | 88 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 121 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 86.0 Mpa |
| Tensile modulus | ISO 527-2/50 | 4500 Mpa | |
| bending strength | ISO 178 | 135 Mpa | |
| Flexural modulus | ISO 178 | 4400 Mpa | |
| bending strength | ASTM D790 | 140 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 88.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.6 % |
| Flexural modulus | ASTM D790 | 4500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 98.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| UL flame retardant rating | 0.830mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| ash content | ISO 3451 | 15 % | |
| density | ASTM D792 | 1.28 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 24 g/10min |
| density | ISO 1183 | 1.28 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ISO 1133 | 24 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/LS-1150G |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 120 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 127 °C | |
| vicat | -- | ISO 306/B120 | 130 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 122 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 123 °C | |
| vicat | -- | ISO 306/B50 | 128 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 128 °C |