Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414B BK1A068 SABIC INNOVATIVE US
LEXAN™
Electrical applications,Home appliance components,Bottle cap
Processability,Moderate liquidity,Ductility,copolymer,Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414B BK1A068 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 77.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 70 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414B BK1A068 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 140 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| TD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B120 | 146 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 139 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C | |
| vicat | -- | ISO 306/B50 | 145 °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 128 °C |
| vicat | ASTM D152510 | 145 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414B BK1A068 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| 屈服 | ASTM D638 | 56.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2230 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| elongation | 断裂 | ASTM D638 | 98 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 92.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 50.0 Mpa |
| bending strength | ISO 178 | 85.0 Mpa | |
| flexural modulus | ISO 178 | 2250 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL1414B BK1A068 |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |