Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 6013L-17 TOPAS GERMANY
TOPAS®
Optical applications
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TOPAS GERMANY/6013L-17 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.0 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2900 Mpa |
| elongation at break | 23°C | ISO 527-2 | 2.8 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 63 Mpa |
| optical performance | Test Condition | Test Method | TOPAS GERMANY/6013L-17 |
|---|---|---|---|
| refractive index | ISO 489 | 1.53 °C | |
| transmittance | 2000μm | ISO 13468-2 | 91 % |
| Flame retardant performance | Test Condition | Test Method | TOPAS GERMANY/6013L-17 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 0.75mm |
| physical property | Test Condition | Test Method | TOPAS GERMANY/6013L-17 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.01 % |
| melt mass-flow rate | 260℃/2.16Kg | ISO 1133 | 14 cm3/10min |
| Thermal performance | Test Condition | Test Method | TOPAS GERMANY/6013L-17 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 130 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 140 °C |