Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 408HS DUPONT USA
Zytel®
Industrial machinery,Automotive sector
enhance,Toughening,Thermal stability,High impact resistance,High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| Limiting Oxygen Index (LOI) | ASTM D-2863 | 50%RH｜20 % |
| thermal performance | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| melting temperature | ASTM D-2177 | 50%RH｜- °C | |
| Fisher Johns法 | ASTM D-789 | 255 °C | |
| brittle temperature | ASTM D-746 | 50%RH｜-84 °C | |
| Linear coefficient of thermal expansion | 平行流动方向 | ASTM E831 | 0.00010 cm/cm/ ℃ |
| ASTM D696/ISO 11359 | 7×10-5 mm/mm.℃ | ||
| Heat Deflection Temperature | 18×106Pa，HDT | ASTM D-648 | 50%RH｜- °C |
| Limiting Oxygen Index | ASTM D2863 | 23 % | |
| melting temperature | 255 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 50%RH｜- m/m/℃ | |
| Heat Deflection Temperature | 66 psi， 未退火，HDT | ASTM D648 | 184 °C |
| Load deformation | 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- % |
| UL flame retardant rating | UL 94 | HB | |
| Heat Deflection Temperature | (0.5)×106Pa，HDT | ASTM D-648 | 50%RH｜- °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| Elongation at break | ASTM D638/ISO 527 | 80 % | |
| Rubbing modulus | 23℃ | ASTM D-790 | 50%RH｜1103 Mpa |
| Impact strength of cantilever beam gap | ASTM D256 | 134 J/m | |
| tensile strength | ASTM D638/ISO 527 | 62.1 kg/cm²(MPa)[Lb/in²] | |
| elongation at yield | ASTM D-638 | 50%RH｜15 % | |
| tensile strength | 屈服 | ASTM D638 | 62.7 Mpa |
| Elongation at break | ASTM D638 | 50 % | |
| 23℃ | ASTM D-638 | 50%RH｜270 % | |
| elongation | ASTM D638/ISO 527 | 60.7 % | |
| flexural modulus | ASTM D790 | 2070 Mpa | |
| Shore hardness | ASTM D-676 | 50%RH｜76 | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 50%RH｜240 J/m |
| Hardness (Rockwell R) | ASTM D-785 | DAM｜R115 | |
| Impact strength of cantilever beam gap | 长试样23℃ | ASTM D-1822 | 50%RH｜1680 kJ/m² |
| 短试样23℃ | ASTM D-1822 | 50%RH｜265 kJ/m² | |
| tensile strength | 23℃，屈服 | 50%RH｜51.7 Mpa | |
| 23℃ | ASTM D-638 | 50%RH｜51.7 Mpa | |
| Hardness (Rockwell M) | ASTM D-785 | 50%RH｜M50 |
| Basic performance | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| Water absorption rate | 饱和(23℃) | ASTM D-570 | 50%RH｜- % |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- % |
| Electrical performance | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| Dissipation Factor | 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 |
| dielectric constant | 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 |
| volume resistivity | ASTM D257/IEC 60093 | 10 Ω.cm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.1 | |
| volume resistivity | ASTM D-257 | 50%RH｜1013 Ω.m | |
| Dissipation Factor | 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 |
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | |
| dielectric constant | 103Hz(cps) | ASTM D-150 | DAM｜3.1 |
| 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 |
| other | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| characteristic | 注塑级.良好的热稳定性 |
| Physical properties | Test Condition | Test Method | DUPONT USA/408HS |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| Water absorption rate | 24小时 | ASTM D570 | 1.2 % |
| 饱和 | ASTM D570 | 7.0 % | |
| ASTM D570/ISO 62 | 1.2 % |