PEI HU1010-1H1000 SABIC INNOVATIVE US
ULTEM™ 
Medical devices、Medical and nursing suppl
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Suspended wall beam without notch impact strength23°CASTM D48121300 J/m
Dart impact23°C, Total EnergyASTM D376333.0 J
Reverse notch impact3.20 mmASTM D2561200 J/m
Dart impact23°CASTM D302933.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Rockwell hardnessM 级ASTM D785109
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Tensile modulus--2ASTM D6383580 Mpa
tensile strength 屈服3ASTM D638110 Mpa
elongation断裂3ASTM D63860 %
bending strength屈服, 100 mm 跨距5ASTM D790165 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮ASTM D104410.0 mg
bending strength--6,7ISO 178160 Mpa
屈服, 50.0 mm 跨距4ASTM D790174 Mpa
Flexural modulus--6ISO 1783300 Mpa
50.0 mm 跨距4ASTM D7903420 Mpa
elongation屈服ISO 527-2/56.0 %
tensile strength 屈服ISO 527-2/5105 Mpa
elongation屈服3ASTM D6387.0 %
tensile strength 断裂3ASTM D638105 Mpa
Flexural modulus100 mm 跨距5ASTM D7903510 Mpa
Tensile modulus--ISO 527-2/13200 Mpa
elongation断裂ISO 527-2/560 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Dissipation Factor1 kHzASTM D1501.3E-3
dielectric strength1.60 mm, in OilASTM D14928 KV/mm
Volume resistivityASTM D2571.0E+17 ohms·cm
Dissipation Factor2.45 GHzASTM D1502.5E-3
dielectric strength1.60 mm, in AirASTM D14933 KV/mm
Hot wire ignition (HWI)UL 746PLC 1
dielectric constant1 kHzASTM D1503.15
arc resistanceASTM D495PLC 5
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 2
Compared to the Leakage Tracking Index (CTI)UL 746PLC 4
High arc combustion index (HAI)UL 746PLC 3
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
UL flame retardant rating0.71 mmUL 94V-2
3.0 mmUL 945VA
0.75 mmUL 94V-0
Limiting Oxygen IndexASTM D286344 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Melt volume flow rate360°C/5.0 kgISO 113325.0 cm3/10min
Water absorption rate平衡, 23°CASTM D5701.3 %
平衡, 23°C, 50% RHISO 620.70 %
melt mass-flow rate337°C/6.6 kgASTM D123818 g/10 min
Water absorption rate饱和, 23°CISO 621.3 %
Shrinkage rate3.20 mm，Flow内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Linear coefficient of thermal expansion流动 : -20 到 150°CASTM E8315.6E-5 cm/cm/°C
横向 : -40°CISO 11359-25.0E-5 cm/cm/°C
RTIUL 746170 °C
Heat distortion temperature0.45 MPa, 未退火, 6.40 mm，HDTASTM D648207 °C
vicat--ISO 306/B120212 °C
--ASTM D152510218 °C
thermal conductivityASTM C1770.22 W/m/K
vicat--ISO 306/B50211 °C
Linear coefficient of thermal expansion流动 : -40 到 40°CISO 11359-25.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm，HDTASTM D648198 °C
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af193 °C
RTI ImpUL 746170 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8315.0E-5 cm/cm/°C
RTI ElecUL 746170 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature350 to 400 °C
drying temperature150 °C
Suggested injection volume40 to 60 %
drying time4.0 to 6.0 hr
Temperature in the middle of the barrel340 to 400 °C
Temperature at the rear of the barrel330 to 400 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder345 to 400 °C
Back pressure0.300 to 0.700 Mpa
Temperature135 to 165 °C
Spray nozzle temperature345 to 400 °C