PEI HU1000-7HD395 SABIC INNOVATIVE US
ULTEM™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 201 °C |
| Linear thermal expansion coefficient | 横向 : -20 到 150°C | ASTM E831 | 5.4E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 5.0E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 5.0E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 215 °C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 215 °C |
| -- | ISO 306/B120 | 211 °C | |
| -- | ASTM D15259 | 218 °C | |
| Linear thermal expansion coefficient | 流动 : -20 到 150°C | ASTM E831 | 5.6E-5 cm/cm/°C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Middle Temperature | 340 到 400 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 150 °C | ||
| Mold Temperature | 135 到 165 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 350 到 400 °C | ||
| Rear Temperature | 330 到 400 °C | ||
| Nozzle Temperature | 345 到 400 °C | ||
| Front Temperature | 345 到 400 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 9.0 g/10 min |
| Melt Volume flow Rate | 220°C/5.0 kg | ISO 1133 | 13.0 cm3/10min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.70 % |
| 平衡, 23°C | ASTM D570 | 1.3 % | |
| 24 hr | ASTM D570 | 0.25 % | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 1.3 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Tensile Modulus | -- | ISO 527-2/1 | 3200 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 60 % |
| 断裂 | ISO 527-2/5 | 60 % | |
| Tensile Strength | 断裂 | ISO 527-2/5 | 85.0 Mpa |
| 屈服 3 | ASTM D638 | 110 Mpa | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 3430 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 3580 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/5 | 6.0 % |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 173 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 7.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 160 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 3300 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/5 | 105 Mpa |
| 断裂 3 | ASTM D638 | 90.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1300 J/m |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 0.00 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Oxygen Index | ASTM D2863 | 47 % |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | 1.0E+17 ohms·cm | |
| Hot-wire Ignition | UL 746 | PLC 1 | |
| Dielectric Constant | 1 kHz | ASTM D150 | 3.15 |
| Dissipation Factor? | 1 kHz | ASTM D150 | 1.3E-3 |
| Arc Resistance | ASTM D495 | PLC 5 | |
| Dielectric Strength | 1.60 mm, in Air | ASTM D149 | 33 KV/mm |
| Comparative Tracking Index | UL 746 | PLC 4 | |
| High Amp Arc Ignition | UL 746 | PLC 3 | |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| Dissipation Factor? | 2.45 GHz | ASTM D150 | 2.5E-3 |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 |