Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP H1700 LG CHEM KOREA
SEETEC
Thin-walled container,Automotive sector,Thin walled containers and meal boxes,Can also be used for automotive modification
Easy to process,Scratch resistant,High rigidity,High crystallinity,Homopolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/H1700 |
|---|---|---|---|
| Rockwell hardness | R-scale | ASTM D785 | 110 |
| Impact strength of cantilever beam gap | 23℃（notched） | ASTM D256 | 4 kg.cm/cm |
| Flexural modulus | ASTM D790 | 21500 Kgf/cm2 | |
| tensile strength | 50mm/min，屈服 | ASTM D638 | 420 Kgf/cm2 |
| 50mm/min，屈服 | ASTM D638 | 41 Mpa | |
| elongation at break | 50mm/min | ASTM D638 | 50 % |
| Flexural modulus | ASTM D790 | 2100 Mpa |
| physical property | Test Condition | Test Method | LG CHEM KOREA/H1700 |
|---|---|---|---|
| density | ASTM D1505 | 0.9 g/cm³ | |
| melt mass-flow rate | 230℃/2.16 kg | ASTM D1238 | 60 g/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/H1700 |
|---|---|---|---|
| Heat distortion temperature | 4.6kgf/cm2，HDT | ASTM D648 | 275 ℉ |
| vicat | 1kgf | ASTM D1525 | 313 ℉ |
| 1kgf | ASTM D1525 | 156 °C | |
| Heat distortion temperature | 4.6kgf/cm2，HDT | ASTM D648 | 135 °C |