PA66 RXR03010 SABIC INNOVATIVE US
--
Electronic and Electrical Applications,Lighting applications
Easy to form,Filler: Glass fiber reinf,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/RXR03010
Dart impact23°C,TotalEnergyASTM D376318.0 J
Impact strength of cantilever beam gap23°CISO 180/1A16 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-24.00 J
Suspended wall beam without notch impact strength23°CISO 180/1U86 kJ/m²
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/RXR03010
Heat Deflection Temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf259 °C
0.45MPa,未退火,3.20mmASTM D648260 °C
1.8MPa,未退火,3.20mmASTM D648253 °C
1.8MPa,未退火,64.0mm跨距ISO 75-2/Af244 °C
Linear coefficient of thermal expansionTD：-30to30°CASTM D6966.2E-05 cm/cm/°C
MD：-30到30°CASTM D6963.2E-05 cm/cm/°C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RXR03010
bending strength断裂,50.0mm跨距ASTM D790337 Mpa
ISO 178229 Mpa
屈服,50.0mm跨距ASTM D790338 Mpa
elongation断裂ASTM D6382.9 %
屈服ASTM D6382.8 %
flexural modulus50.0mm跨距ASTM D79012400 Mpa
ISO 17811200 Mpa
Tensile modulusASTM D63813900 Mpa
ISO 527-2/114100 Mpa
Tensile strain断裂ISO 527-2/52.9 %
屈服ISO 527-2/52.9 %
tensile strength断裂ISO 527-2/5232 Mpa
屈服ASTM D638230 Mpa
屈服ISO 527-2/5232 Mpa
断裂ASTM D638210 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RXR03010
shrinkage rateMD：24小时ASTM D9550.20-0.40 %
TD：24hrASTM D9551.0-3.0 %
Water absorption rate24hr,50%RHASTM D5700.66 %
平衡,23°C,50%RHISO 621.0 %