Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS ABS P2L-AT ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 4.0 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 70 kJ/m² |
| hardness | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 120 MPa |
| Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 45.0 MPa |
| Flexural modulus | 23°C | ISO 178 | 2550 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.1 % |
| 断裂,23°C | ISO 527-2/50 | >15 % | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2700 MPa |
| bending strength | 23°C | ISO 178 | 72.0 MPa |
| Electrical performance | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 31 kV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| 23°C,100Hz | IEC 60250 | 3.10 | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 8E-03 |
| 23°C,1MHz | IEC 60250 | 8E-03 |
| flammability | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| burning rate | 2.00mm | ISO 3795 | 65 mm/min |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 45.0 cm³/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.40to0.60 % |
| MD | ISO 294-4 | 0.40to0.60 % |
| Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./ABS P2L-AT |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 92.0 °C |
| vicat | ISO 306/B50 | 96.0 °C | |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 96.0 °C |