POP 8102 SABIC INNOVATIVE KOREA
SABIC® COHERE™ 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE KOREA/8102
Shore hardness邵氏 D, 1 秒ASTM D224040
邵氏 A, 1 秒ASTM D224092
filmTest ConditionTest MethodSABIC INNOVATIVE KOREA/8102
Initial sealing temperature吹塑薄膜内部方法80.0 °C
elongationTD : 断裂, 50 µm, 吹塑薄膜ASTM D882620 %
Secant modulus1% 正割, MD : 50 µm, 吹塑薄膜ASTM D88268.0 Mpa
tensile strength TD : 断裂, 50 µm, 吹塑薄膜ASTM D88242.0 Mpa
Elmendorf tear strengthTD : 50.0 µmASTM D192217 g/µm
MD : 50.0 µmASTM D192210 g/µm
Secant modulus1% 正割, TD : 50 µm, 吹塑薄膜ASTM D88276.0 Mpa
tensile strength MD : 断裂, 50 µm, 吹塑薄膜ASTM D88247.0 Mpa
elongationMD : 断裂, 50 µm, 吹塑薄膜ASTM D882600 %
Dart impact50 µm, 吹塑薄膜ASTM D1709> 1000 g
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE KOREA/8102
tear strengthASTM D6248.53 Mpa
elongation断裂ASTM D638800 %
tensile strength 断裂ASTM D63824.5 Mpa
Flexural modulus% 正割ASTM D79082.4 Mpa
optical performance Test ConditionTest MethodSABIC INNOVATIVE KOREA/8102
Haze ratioASTM D10034.0 %
physical property Test ConditionTest MethodSABIC INNOVATIVE KOREA/8102
melt mass-flow rate190°C/2.16 kgASTM D12381.0 g/10 min
Mooney viscosityML 1+4, 121°CASTM D164620 MU
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE KOREA/8102
melting temperature内部方法98.0 °C
Glass Transition Temperature内部方法-31.0 °C