PA66 70G43L NC010 DUPONT SHENZHEN
Zytel® 
Electrical field、Electronic field、Fitness equipment
Glass fiber reinforced、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Suspended wall beam without notch impact strength-30°CISO 180/1U110 kJ/m²
23°CISO 180/1U110 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
-30°CISO 179/1eU85 kJ/m²
hardnessTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Rockwell hardnessM 计秤ISO 2039-2105
R 计秤ISO 2039-2125
Mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Tensile creep modulus1000 hrISO 899-1-- Mpa
Tensile modulusISO 527-214000 Mpa
bending strengthISO 178340 Mpa
Tensile strain断裂ISO 527-23.0 %
Flexural modulusISO 17812000 Mpa
tensile strength 断裂ISO 527-2225 Mpa
Tensile creep modulus1 hrISO 899-1-- Mpa
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Dissipation Factor100 HzIEC 62631-2-10.010
1 MHzIEC 62631-2-10.015
dielectric strengthIEC 60243-127 KV/mm
Volume resistivityIEC 62631-3-1> 1.0E+13 ohms·m
relative permittivity1 MHzIEC 62631-2-14.10
Surface ResistivityIEC 62631-3-2-- ohms
relative permittivity100 HzIEC 62631-2-14.50
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
UL flame retardant ratingUL 94HB
Limiting Oxygen IndexISO 4589-223 %
FMVSS combustion rateFMVSS 302B
burning rate1.00 mmISO 379527 mm/min
Filling analysisTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Ejection Temperature210 °C
Thermal Conductivity of Melt0.25 W/m/K
Melt density1.29 g/cm³
Specific Heat Capacity of Melt2050 J/kg/°C
physical property Test ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Water absorption rate饱和, 23°C, 2.00 mmISO 624.7 %
平衡, 23°C, 2.00 mm, 50% RHISO 621.5 %
24 hr, 23°C, 2.00 mmISO 620.90 %
Shrinkage rate流量ISO 294-40.30 %
横向流量ISO 294-41.0 %
Thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
melting temperatureISO 11357-3262 °C
Linear coefficient of thermal expansion横向 : -40 到 23°CISO 11359-26.1E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火，HDTISO 75-2/B262 °C
Linear coefficient of thermal expansion流动 : -40 到 23°CISO 11359-22.0E-5 cm/cm/°C
Effective thermal diffusivity coefficient9.50E-8 m²/s
Linear coefficient of thermal expansion流动 : 55 到 160°CISO 11359-29.0E-6 cm/cm/°C
vicatISO 306/B50255 °C
Heat distortion temperature1.8 MPa, 未退火，HDTISO 75-2/A255 °C
Linear coefficient of thermal expansion横向 : 55 到 160°CISO 11359-21.3E-4 cm/cm/°C
流动ISO 11359-21.5E-5 cm/cm/°C
横向ISO 11359-27.9E-5 cm/cm/°C
Glass Transition TemperatureISO 11357-280.0 °C
injectionTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
pressure holding50.0 to 100 Mpa
Maximum Screw Tangential Speed12 m/min
pressure holdingDrying Recommendedyes
Suggested maximum moisture content0.20 %
Drying time - hot air dryer2.0 to 4.0 hr
Processing (melt) temperature285 to 305 °C
drying temperature80 °C
Temperature70 to 120 °C
Melt Temperature, Optimum295 °C
Hold Pressure Time3.00 s/mm
Mold Temperature, Optimum100 °C