Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 95G40 BK031 DUPONT USA
Zytel®
electrical equipment,Fitness equipment
High temperature resistan,Glass fiber reinforced,Filler: Glass fiber reinf,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 110 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 8.1E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1.4E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 4E-06 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 9.1E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 263 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| bending strength | ISO 178 | 277 Mpa | |
| flexural modulus | ISO 178 | 10000 Mpa | |
| Tensile modulus | ISO 527-2 | 11300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| tensile strength | 断裂 | ISO 527-2 | 175 Mpa |
| other | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| characteristic | 耐高温.玻纤40%增强注塑级 | ||
| Color | 黑色 | ||
| purpose | 专业用于电子电器零配部件增强性能材料 |
| Physical properties | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| Ejection Temperature | 210 °C | ||
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % |
| flammability | Test Condition | Test Method | DUPONT USA/95G40 BK031 |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| FMVSS flammability | FMVSS302 | B |