EVA UE629 Taiwan Polymer
--
Sole foaming
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | Taiwan Polymer/UE629 |
|---|---|---|---|
| film thickness | TD | ASTM D-638/D-882 | 240 kg/cm2 |
| TD | ASTM D-638/D-882 | 640 % | |
| Casting film forming | ASTM D-638/D-882 | 750 % | |
| melting temperature | ASTM D-2117 | 86 ℃ | |
| film thickness | MD | ASTM D-638/D-882 | 480 % |
| density | ASTM D-1505 | 0.939 g/cm3 | |
| emit | ASTM D-638/D-882 | 117 kg/cm2 | |
| ASTM D-638/D-882 | 220 % | ||
| film thickness | MD | ASTM D-638/D-882 | 250 kg/cm2 |
| melt mass-flow rate | ASTM D-1238 | 2.5 g/10min | |
| Casting film forming | ASTM D-638/D-882 | 180 kg/cm2 | |
| Low temperature brittleness temperature | ASTM D-746 | <-76 ℃/F50 | |
| Shore hardness | ASTM D-2240 | 31 Shore D | |
| Vinyl acetate content | ASTM USIFE | 18 % | |
| vicat | ASTM D-1525 | 64 ℃ |
| Mechanical properties | Test Condition | Test Method | Taiwan Polymer/UE629 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-1709 | 430 G/F50 |