Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS C-200SC IDEMITSU JAPAN
--
--
currency、Filler: Glass mineral、65% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 8.3 kJ/m² |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Flowability2 | 1.00mm，Flowability | 内部方法 | 125 mm |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 101 |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric constant | IEC 60250 | 4.70 | |
| dielectric strength | 3.00mm | IEC 60243-1 | 14 KV/mm |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| bending strength | ISO 178 | 212 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.1 % |
| Flexural modulus | ISO 178 | 19500 Mpa | |
| tensile strength | ISO 527-2 | 135 Mpa |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| UL flame retardant rating | 0.750mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | >0.020 % |
| density | ISO 1183 | 1.95 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/C-200SC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 274 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
| TD | ISO 11359-2 | 2.3E-05 cm/cm/°C |