PBT+PET VALOX™ V8030CS resin 沙伯基础
--
家电部件,把手,护罩
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest Method沙伯基础/VALOX™ V8030CS resin
Charpy Notched Impact Strength23°CISO 179/1eA24 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25658 J/m
-30°CISO 180/1A4.0 kJ/m²
23°CISO 180/1A4.1 kJ/m²
Mechanical propertiesTest ConditionTest Method沙伯基础/VALOX™ V8030CS resin
tensile strength 屈服ISO 527-2/595.0 MPa
elongation断裂3ASTM D6382.8 %
断裂2ASTM D6388.6 %
屈服ASTM D6382.7 %
Tensile strain屈服ISO 527-2/52.1 %
tensile strength 屈服ASTM D63899.0 MPa
Flexural modulusISO 1785480 MPa
bending strengthISO 178148 MPa
tensile strength 断裂ISO 527-2/5103 MPa
bending strength屈服,50.0mm跨距ASTM D790148 MPa
tensile strength 断裂ASTM D63898.0 MPa
Tensile modulusASTM D6386180 MPa
Tensile strain断裂ISO 527-2/52.0 %
Flexural modulus50.0mm跨距ASTM D7905580 MPa
Fracture bending strainISO 1783.4 %
Tensile modulusISO 527-2/15890 MPa
bending strength断裂,50.0mm跨距ASTM D790148 MPa
physical property Test ConditionTest Method沙伯基础/VALOX™ V8030CS resin
densityASTM D7921.43 g/cm³
ISO 11831.43 g/cm³
Melt volume flow rate265°C/2.16kgISO 113329.0 cm³/10min
265°C/5.0kgISO 113375.0 cm³/10min
Thermal performanceTest ConditionTest Method沙伯基础/VALOX™ V8030CS resin
vicat--ISO 306/A120222 °C
Hot deformation temperature (HDT)1.8MPa,未退火,3.20mm，HDTASTM D648173 °C
vicat--ISO 306/A50222 °C
ASTM D15258224 °C
Hot deformation temperature (HDT)0.45MPa,未退火,3.20mm，HDTASTM D648220 °C