POM 900P DUPONT THAILAND
Delrin® 
Fiber grade,Thin walled products
wear resistant,High rigidity,high strength,enhance,High impact resistance,High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodDUPONT THAILAND/900P
Rockwell hardnessM-SaleISO 2039-292
R-SaleISO 2039-2120
Supplementary InformationTest ConditionTest MethodDUPONT THAILAND/900P
EmissionVDA275<8.00 mg/kg
EmissionofOrganicCompoundsVDA2774.30 µgC/g
thermal performanceTest ConditionTest MethodDUPONT THAILAND/900P
AnnealingTemperature160 °C
AnnealingTime-Optional30.0 min/mm
Effective thermal diffusivity coefficient8E-08 m²/s
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B162 °C
1.8MPa,UnannealedISO 75-2/A94.0 °C
Linear coefficient of thermal expansionTDISO 11359-21.2E-04 cm/cm/°C
MD：23to55°CASTME8311E-04 cm/cm/°C
MDISO 11359-21.2E-04 cm/cm/°C
Melting temperatureISO 11357-3178 °C
Vicat softening temperatureISO 306/B50160 °C
mechanical propertiesTest ConditionTest MethodDUPONT THAILAND/900P
Bending modulusISO 1783000 Mpa
Friction coefficientvs.Itself-Dynamic,1hrASTM D18940.25
Nominal tensile fracture strainISO 527-223 %
Tensile creep modulus1hrISO 899-12800 Mpa
1000hrISO 899-11500 Mpa
Tensile modulusISO 527-23300 Mpa
Tensile strainYieldISO 527-212 %
tensile strengthYieldISO 527-271.0 Mpa
Electrical performanceTest ConditionTest MethodDUPONT THAILAND/900P
Compared to the anti leakage trace indexIEC 60112PLC 0
Hot wire ignition0.750mmUL 746PLC 4 sec
Relative permittivity100HzIEC 602503.80
1MHzIEC 602503.80
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 600931E+14 ohms·cm
Physical propertiesTest ConditionTest MethodDUPONT THAILAND/900P
densityISO 11831.42 g/cm³
melt mass-flow rateISO 113325 g/10min
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 113321.0 cm3/10min
Shrinkage rateMDISO 294-41.9 %
TDISO 294-41.9 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.40 %
Saturation,23°C,2.00mmISO 621.4 %
impact performanceTest ConditionTest MethodDUPONT THAILAND/900P
Charpy Notched Impact Strength23°CISO 179/1eA8.0 kJ/m²
-30°CISO 179/1eA7.0 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A8.0 kJ/m²
23°CISO 180/1A7.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU200 kJ/m²
23°CISO 179/1eU200 kJ/m²
flammabilityTest ConditionTest MethodDUPONT THAILAND/900P
AtomizationG-value(condensate)ISO 64522E-04 g
F-value(refraction)ISO 645295 %
Burning rate1.00mmISO 379520 mm/min
Extreme Oxygen IndexISO 4589-223 %
FMVSS flammabilityFMVSS302B
UL flame retardant rating0.8mmIEC 60695-11-10,-20HB
1.5mmIEC 60695-11-10,-20HB
0.8mmUL 94HB
1.5mmUL 94HB