Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 201-G30 202 FNA NANTONG ZHONGLAN
BLUESTAR®
Electrical field、Electronic field、Plastic connectors、Automotive sector、Industrial machinery、Lighting applications、Electrical/Electronic App
Glass fiber reinforced、Processability、High rigidity、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 60.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.3E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.3*10e16 Ω.cm |
| Mechanical properties | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 7.5 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 180 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638 | 10500 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 8000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790 | 180 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 115 Mpa |
| Flexural modulus | ASTM D790 | 8000 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 110 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| characteristic | 30%玻璃纤维增强.3.0mm阻燃 V-0.性能与长春4830相当 | ||
| Color | 本色 | ||
| purpose | 连接器.线圈骨架.散热风扇等 |
| Physical properties | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.62 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 15-25 g/10min |
| flammability | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| processability | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| process temperature | 240-270 °C | ||
| pressure | 70-120 Mpa | ||
| Dry conditions | 120-140℃ 3-4h | ||
| screw speed | <100 rpm | ||
| Melt Temperature | 250-280 °C | ||
| Temperature | 60-80 °C |
| physical property | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.16 % |
| Shrinkage rate | TD | ASTM D955 | 0.60 % |
| Thermal performance | Test Condition | Test Method | NANTONG ZHONGLAN/201-G30 202 FNA |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 208 °C |
| Combustibility (rate) | UL 94 | V-0 3.0mm | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 220 °C |
| HDT | ASTM D648/ISO 75 | 220 ℃（℉） |