PC/ABS AC2400 FCFC TAIWAN
TAIRILOY®
Electrical field,Electronic field,Household appliances,Household appliances,Automotive sector
High mobility
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC2400 |
|---|---|---|---|
| Rockwell hardness | 23℃ | ISO 2039/2 | 110 R |
| bending strength | 23℃ | ISO 178 | 84 MPa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D785 | 55 kg.cm/cm |
| Flexural modulus | 23℃ | ISO 178 | 2550 MPa |
| bending strength | 23℃ | ASTM D790 | 850 Kg/cm2 |
| tensile strength | 23℃ | ISO 527 | 49 MPa |
| 23℃ | ASTM D638 | 500 Kg/cm2 | |
| Impact strength of cantilever beam gap | 23℃,1/8'' 厚 | ISO 180 | 539 J/m |
| Flexural modulus | 23℃ | ASTM D790 | 26000 Kg/cm2 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC2400 |
|---|---|---|---|
| density | 23℃ | ISO 1183 | 1.13 |
| Shrinkage rate | 3.2mm | ASTM D995 | 0.4－0.6 % |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC2400 |
|---|---|---|---|
| Heat distortion temperature | 18.6kg/cm2，HDT | ISO 75/A | 98 ℃ |
| vicat | 9.8N | ISO 306 | 122 ℃ |
| UL flame retardant rating | UL94 | HB | |
| melt mass-flow rate | 240℃×5Kg | ISO 1133 | 8 g/10min |